Fish farming is becoming an increasingly popular agricultural activity, and water quality in these environments is a major concern. Fish parasites, such as monogeneans, respond to changes in abiotic conditions, either with an increase or decrease in population. This study aimed to identify gill monogeneans and analyse their relationships with abiotic factors during the ontogenetic development of Nile tilapia over the fish culture cycle in Mato Grosso do Sul, Brazil. Fish were sampled monthly for eight months, and a total of 200 fish were collected. The physical and chemical water parameters were measured and correlated with the abundance of each monogenean species. Over the fish culture cycle, the physical and chemical parameters fluctuated, and the water quality decreased. The parasites found included Cichlidogyrus tilapiae, Cichlidogyrus thurstonae, Cichlidogyrus sclerosus, Cichlidogyrus halli and Scutogyrus longicornis. The abundances of all species showed significant differences during ontogenetic development (body size) and C. tilapiae, C. sclerosus, C. thurstonae and S. longicornis were correlated with changes in abiotic conditions. However, C. halli was not significantly correlated with any of the evaluated physical or chemical parameters. Understanding how different monogenean species respond to changes in the physical and chemical parameters of water during a production cycle can prevent peaks in abundance and subsequent sanitary problems.

Thermoluminescence emission on lead oxychloroborate glasses under UV exposure.

Glassy materials were prepared using two different systems: 50B2 O3 - (50 - x)PbO - xPbCl2, with x = 0, 2 and 5 in mol % (System BPCl-I) and 50BO1.5 - (50 - x)PbO - xPbCl2 with x = 0, 2, 5 and 7 in cationic % (System BPCl-II). Structural and optical characterization showed that PbCl when substituted for PbO changed the structure of the glass network by replacing nonbridging oxygens for chlorine ions. This substitution also caused a change in the number of defects responsible for thermoluminescence (TL) emission (electrons and hole trap centres). Thermoluminescence emissions were observed for the first time in lead oxychloroborate glasses after exposure to UV radiation. Sample BPCl-I-2 (x = 2 from System I) demonstrated better TL emission compared with other glass samples. One intense peak in the glow curve, centred at ~122°C followed by a shoulder at ~180°C, was highly sensitive to UV radiation. There were also good linear responses at dose range ~0.4 to ~2 J/cm2 for the first peak (low temperature) and ~0.4 to ~4 J/cm2 for the second peak (high temperature).